Mono Coat RM 4503
Code: RM4503
Description: Mono-Coat® RM-4503 is a semi-permanent, general use solventbased release system for rotation molding applications. Mono Coat RM 4503 provides high-temperature stability as well as abrasion resistance on the release film. It also adheres to the mold surface and provides multiple releases with minimum transfer to molded parts. Mono Coat RM 4503 leaves virtually no buildup on the mold when applied according to instructions.
Temprature Range - Do not store at temperatures above 40°C/104°F. Keep container tightly sealed to prevent evaporation and/or contamination.
Application – Highly Polished Molds
- Thoroughly clean the area to be treated to remove any previous release agent or other buildup. Then wipe with a clean solvent or naphtha and let air dry.
- Saturate (not dripping) a clean, 100% cotton cloth and wipe on a smooth continuous film. Apply to no more than a few square feet at a time.
- When the film begins to evaporate at the edge (See Notes: below), wipe the surface with a second clean, dry, cotton cloth. Use a circular motion from the outside, working inwards until film is left dry and clear.
- Continue working in this way until the entire mold surface has been coated.
- Repeat this procedure 4 times, making a total of 5 coats, allowing 15 minutes between each coat.
- Allow 30 minutes after the last coat for full cure at room temperature*. Proceed with production.
Application – Regular Finish Molds
- Clean the mold as in the previous section
- Apply a small amount of product to a clean, 100% cotton cloth; wipe onto the mold surface to form a glossy continuous film.
- As soon as the wiping action appears not to be forming a film, add more Mono Coat RM 4503 to the cloth, to ensure it wets the surface of the mold as described in step #2 above.
- Continue working in this way until the entire mold surface has been coated.
- Repeat this procedure 2 times, making a total of 3 coats, allowing 15 minutes between each coat.
- Allow 30 minutes after the last coat for full cure at room temperature*. Proceed with production.
Packaging - Mono Coat RM 4503 is available in a variety of package sizes. Please contact Novanative India for details.
Mono Coat RM 4503 is a semi-permanent, general use solventbased release system for rotation molding applications. Mono Coat RM 4503 provides high-temperature stability as well as abrasion resistance on the release film. It also adheres to the mold surface and provides multiple releases with minimum transfer to molded parts. Mono Coat RM 4503 leaves virtually no buildup on the mold when applied according to instructions.
Do not store at temperatures above 40°C/104°F. Keep container tightly sealed to prevent evaporation and/or contamination.
Application – Highly Polished Molds
- Thoroughly clean the area to be treated to remove any previous release agent or other buildup. Then wipe with a clean solvent or naphtha and let air dry.
- Saturate (not dripping) a clean, 100% cotton cloth and wipe on a smooth continuous film. Apply to no more than a few square feet at a time.
- When the film begins to evaporate at the edge (See Notes: below), wipe the surface with a second clean, dry, cotton cloth. Use a circular motion from the outside, working inwards until film is left dry and clear.
- Continue working in this way until the entire mold surface has been coated.
- Repeat this procedure 4 times, making a total of 5 coats, allowing 15 minutes between each coat.
- Allow 30 minutes after the last coat for full cure at room temperature*. Proceed with production.
Application – Regular Finish Molds
- Clean the mold as in the previous section
- Apply a small amount of product to a clean, 100% cotton cloth; wipe onto the mold surface to form a glossy continuous film.
- As soon as the wiping action appears not to be forming a film, add more Mono Coat RM 4503 to the cloth, to ensure it wets the surface of the mold as described in step #2 above.
- Continue working in this way until the entire mold surface has been coated.
- Repeat this procedure 2 times, making a total of 3 coats, allowing 15 minutes between each coat.
- Allow 30 minutes after the last coat for full cure at room temperature*. Proceed with production.
Typical Properties:
| Appearance | Clear colorless fluid |
| Density, lbs/gal; kg/l | 6.00; 0.72 |
| Flash Point, °F/°C | 19.0/-7.2 |
| Storage Stability, unopened | 12 months |